经典的金相组织照片(会员"leomet"的合集)

leomet · 发表于 2015-8-7 08:48:03

上面是S50C, Austempered. 這個也是, 彩蝕後如下:

leomet · 发表于 2015-8-7 08:52:50

雅圖共賞, 希望你看不厭.

leomet · 发表于 2015-8-11 18:55:00

本帖最后由 leomet 于 2015-8-11 19:00 编辑

亞共晶鑄鋁 hypo-eutectic cast aluminum alloy for engine block

leomet · 发表于 2015-8-15 00:49:31

本帖最后由 leomet 于 2016-9-21 09:39 编辑

稍重蝕. Si 顆粒凸出基地. 像不像沙灘上的石塊?

看完以下漂亮照片, 你應該不反對有人叫我"台灣第一名".

leomet · 发表于 2015-8-29 11:26:11

本帖最后由 leomet 于 2015-9-13 19:02 编辑

Bearing steel, 52100, SUJ 2, Austenized at 1150C and Q and T.
Heating at such a high temp purposely to obtain coarse grains for easier photo taking.

Fully Martensitic structure.

leomet · 发表于 2015-8-29 11:26:12

Bearing steel, 52100, SUJ 2, Austenized at 1150C and Q and T.

Fully Martensitic structure.

leomet · 发表于 2015-8-29 11:37:10

52100, 這個是冷速不足的試片. 晶界有非M出現.

leomet · 发表于 2015-8-29 11:37:11

本帖最后由 leomet 于 2015-8-29 12:06 编辑

52100, 這個是冷速不足的試片. 晶界有非M出現.
52100是過共析鋼, 所以最早出現在晶界的是Carbide, 再來是 P and B. 這些都叫 "非M". ---non-Martensitic

ustbzt · 发表于 2015-9-4 10:12:10

十分精美的金相照片，学习了！

伯龙马 · 发表于 2015-9-4 10:28:48

十分精美的金相照片，谢谢了！但是，遗憾外文看不懂。

luoxz1990 · 发表于 2015-9-4 23:06:03

挺好的学习学习啦字数不够

leomet · 发表于 2015-9-13 19:05:28

伯龙马发表于 2015-9-4 10:28
十分精美的金相照片，谢谢了！但是，遗憾外文看不懂。

馬老年少時學俄文? ....................

leomet · 发表于 2015-9-13 19:15:23

cylinder liner 金相.............

leomet · 发表于 2015-9-13 19:15:23

cylinder liner 金相.............

leomet · 发表于 2015-9-13 19:23:04

0.60%C steel for coldworking.

Spheroidized carbide particles in the matrix of Ferrite.

Note the fine grain size of Ferrite.

leomet · 发表于 2015-9-13 19:23:04

本帖最后由 leomet 于 2017-12-9 13:54 编辑

0.60%C steel for coldworking. Bicycle chain material.

Spheroidized carbide particles (tinted pale blue) in the matrix of Ferrite.

Note the fine grain size of Ferrite. << 10 um.

青青园中葵 · 发表于 2015-9-17 22:38:15

leomet 发表于 2008-7-1 21:01
有後進問: 如何分辨磷共晶與碳化物. 今天照了一組相片剛好又有這兩樣東西. 覺得效果不錯, 上傳給從事金 ...

大师，您太厉害了！！！崇拜！！

leomet · 发表于 2015-10-4 10:56:51

本帖最后由 leomet 于 2015-10-10 19:00 编辑

放幾張H13 Q/T 輕蝕照片

Carbide particles dispersed in the matrix of tempered Martensite.

This matrix- type hotwork tool steel is well-known for its toughness.

leomet · 发表于 2015-10-10 18:55:28

本帖最后由 leomet 于 2015-10-11 14:17 编辑

c.p. 0.8%; 870Cx30min; quenched in salt bath at 280C.

Too much R.A. & untempered Martensite in the surface led to poorer strength than those with no R.A.

Workpiece? It's a hush-hush.

leomet · 发表于 2015-10-10 19:09:49

本帖最后由 leomet 于 2015-10-18 18:04 编辑

CPM 10V P/M HS steel, Quenched, not tempered.

Coalescence of some carbide particles indicates that its Austenization temperature is a bit too high.

		自动登录	找回密码
密码			免费注册

[原创] 经典的金相组织照片(会员"leomet"的合集)

本帖子中包含更多资源

本帖子中包含更多资源

评分

本帖子中包含更多资源

本帖子中包含更多资源

评分

本帖子中包含更多资源

评分

本帖子中包含更多资源

评分

点评

本帖子中包含更多资源

评分

本帖子中包含更多资源

评分

本帖子中包含更多资源

本帖子中包含更多资源

评分

本帖子中包含更多资源

评分