失效及缺陷组织照片

leomet

FT, grey iron, with carbide tinted.

leomet

FT, high CE%, lots of graphite flakes in the matrix of Ferrite.

zyb123abc

很有参考意义，不清楚的时候可以对照一下。

leomet

QT內的枝晶間碳化物.

leomet

These photos took me 2 hours' labor.

P/M HSS punch for P/M gear compaction.

leomet

照片是報告中擷取下來的. 這種水平, 也敢執業收費,(權威單位, 收費還不低呢), 老先生我, 看了都要生氣.

照片中紅色橢圓, 說是裂源, 是錯誤的. 它們是終裂處(crack exits)

照片 連 0d 中, 我加的黃色小箭頭所指的乳凸狀圓心, 才是裂源. 疲勞貝紋以此為圓心往外擴延, 你看得岀來嗎?

leomet

這一篇也不行. 沒有指出"root cause".

應該做金相檢驗的. 只照幾張SEM 就敷衍得過? 欺負外行人!

ustbzt

Leomet先生，上传的照片真是宝贵的精神财富，谢谢前辈！

leomet

ustbzt 发表于 2015-7-31 21:45
Leomet先生，上传的照片真是宝贵的精神财富，谢谢前辈！

Beauty is to the eye of the beholder. I am glad you enjoy these photos.

Some people think of them as "gaudy".

leomet

接 http://www.rclbbs.com/forum.php? ... page%3D1&page=2

Very lousy microstructure from a JIS 420 J2 stainless steel ingot.

Most of you barely have the chance to see this.
So I took lots of time to edit these photos for u.

Those twins  appeared after hot forging at too high a temperature.

說那些双晶界是我製樣不到位所產生的劃痕的同行, 看法修正了嗎?

leomet

該試片放了近一年, 拿出來再拍一些晶界碳化物照片.

實在太精彩了, 所以上傳這麼多張.

晶界碳化物旁邊無碳化物微粒出現的區域, 都稱"無 微粒/析出物 區"--- PDZ. Precipitate Depleted Zone, or PFZ, Precipitate Free zone.

因為solute 都聚到晶界上了, 附近當然沒有微粒析出. 有人指正我, PDZ/PFZ只能用在鋁合金, 我也懶得改正了.
It realy doesn't matter much.

使用物鏡是 Olympus MPLFLN100XBD. 8-6 Edeex 公司新購入, 花1.7W RMB, 解析度很好. 舊的一個只值1.0W RMB.
今後1000X照片會更清晰, 大家有眼福了.

ustbzt

谢谢leomet前辈，编辑这些照片真需要下很多功夫呀！

leomet

ustbzt 发表于 2015-8-8 21:05
谢谢leomet前辈，编辑这些照片真需要下很多功夫呀！

是花很多時間, 不過這兩天強烈颱風來襲, 也不能出門. 整理些美照, "傳諸後世", 也是好事一樁.

前面我說過 These photos are my footprints on the sand  of time, in the field of Metallurgy.

I hope you guys enjoy reading them.

附件是我對一篇錯誤的破損分析的評論. 就是這塊鋼材. 出錯誤報告的單位是XX中心, 我30+年前任職過. 在台灣算是金屬方面的權威單位. 可惜現在沒有老和尚. 裏面都是小和尚.

leomet

新舊物鏡照片比較.  滲碳區 殘A. 注意殘A邊界的清析度.

10年前我賣過大陸製金相顯微鏡, 一台進價 < 1W RMB.

ustbzt

I am very enjoy these beautiful  photos and I think most of guys enjoy reading them.
It is difficult to make the metallograph to so excellent. Now, most of guys do not like to take so much time to do it.

chaijiadashao

彩色的金相照片就是漂亮，没得说，以后要多练习搞好彩色金相图片，培养热处理的艺术情趣

leomet

又是這塊 有Twin Boundary Carbide的 420 J2 不銹鋼原材料.
There is nothing new under the Sun.
There are still lots of things you have not yet learned before you retire from your job.
So, do not say it is not possible. Learn to be open-minded.

leomet

Twin Boundary in 420 J2 stainless tool steel.
那些平形直線 可不是刮痕, 磨痕.

They are Twin boundaries. Do not be suspicious. Because you will learn, someday.

http://www.rclbbs.com/forum.php? ... p;extra=#pid1796397

leomet

Twin Boundary in 420 J2 stainless tool steel.
那些平形直線 可不是刮痕, 磨痕.

說是刮痕的同行, 看了這麼多相片後, 不知改變看法沒?

說不可能是Twin的小朋友, 勿執著於420 J2 是BCC metal. 它也有FCC的時候, 你說呢?

leomet

這個H13 曲軸 熱鍛模, 打3模就裂成兩半.
大家看看它的"短命(金)相".
另一付模具, 熱處理條件相同, 用德國料, 正常使用中.

SKD 61 昰需要高韌性的基地型(matrix-type)的模具鋼. 基地上如果出現碳化物顆粒, 韌性就劣化
-----尤其是如果這些碳化物排列成長線條時. 碳化物這樣排列, 就像印刷紙張上製出的 "車縫線". 合金鋼廠品管人員, 這個觀念要記起來, 千萬不要做出這樣的鋼材害人.